Composition in method for treating teeth

ABSTRACT

In accordance with the invention there is provided a method, and a composition for the practice of the method, for repairing tooth or bone structure wherein there is applied to the tooth or bone tissue a composition comprising a polymerized or polymerizable organic phosphoryl monofluoride thereby to attain a strong bond to the tooth or bone tissue.

United States Patent Plymale [451 May 13, 1975 COMPOSITION IN METHOD FOR TREATING TEETH Richard W. Plymale, 1480 Griffin Rd., Davison, Mich. 48423 Filed: Apr. 1, 1971 Appl. No.: 130,438

Inventor:

US. Cl. 32/15; 106/35; 260/952; 264/269 Int. Cl A61k 5/00 Field of Search 264/19, 269; 106/35; 260/952; 32/15 References Cited UNITED STATES PATENTS 6/1966 Shelley 106/35 3,503,128 3/1970 Boyd et a1 106/35 Primary ExaminerDona1d J. Arnold Assistant Examiner-Gene Auville Attorney, Agent, or FirmReising, Ethington & Perry [57] ABSTRACT 16 Claims, N0 Drawings COMPOSITION lN METHOD FOR TREATING TEETH This invention relates to a method and composition for treating diseased, decayed or damaged tooth or bone structure and, more particularly for repairing tooth or bone structure by application of a composition which assures the attainment of a strong bond with the tissue. The invention has particular utility for the repair or filling of tooth cavities and hence will be described in its details principally in conjunction therewith though, as will be mentioned hereinafter, the invention finds numerous other uses in the dental and medical sciences.

When caries is discovered in a tooth, the dentist removes the diseased tooth substance, cleans out the cavity in the tooth formed by such removal, and then shapes the cavity to the best form to receive and retain a filling, all based on accepted principles well known in the art of dentistry. At the present state of the art, none of the dental restorative or filling materials used have a significant degree of chemical or physical adhesion to the hard tooth tissues and hence retention of the filling material is dependent upon mechanical locking. This frequently requires the removal of healthy tooth structure for providing recesses in the tooth to better assure mechanical retention of the filling material. The filling materials presently in use, because they do not provide a strong and permanent bond to the hard tooth tissues, frequently permit bacteria to reach under the filling after a period of time and hence result in further decay at the tooth-filling interface.

It is a principal object of the present invention to pro vide an improved process and composition for the restoration of diseased or otherwise damaged or defective teeth which assures an excellent leak-resistant bond between the filling material and the hard tooth tissue thereby to solve the aforesaid problem. Another and attendant object of the invention is the provision of a composition and method for lining a tooth cavity to assure an excellent bond and seal to the tooth structure and also to the body of filler material used to fill the lined cavity.

Briefly, these objects are accomplished, in accordance with the preferred embodiment of the invention, by lining the cavity, after the diseased tissue had been removed and after the cavity has been thoroughly cleansed, with a composition comprising a polymeriz able organic phosphoryl monofluoride. More specifically, in the preferred embodiment the material used for the lining comprises an organic ester of monofluorophorophosphoric acid wherein the organic radical is unsaturated, i.e., contains at least one carbonto-carbon double bond, whereby it is polymerizable by additional polymerization. Hence, the lining material has the formula wherein R is an unsaturated addition polymerizable group. As will be seen from the more detailed description set forth hereinafter, the preferred liner incorporates a methacrylic group or groups to provide the polymerization though other unsaturated addition polymerizable groups may be used if desired. It should be pointed out that by the term polymerizable is not meant that the compound is necessarily entirely in monomeric form at the time of application of the composition to the tooth since it is within the purview of the invention that the organic phosphoryl monofluoride be in polymeric form, or at least partially polymerized, prior to application to the tooth and the invention as herein described is intended to comprehend such embodiments. However, in the preferred embodiment the organic phosphoryl monofluoride, though not neces sarily totally in monomeric form, is in a form whereby there can be polymerization, or further polymerization, in situ, on the tooth after application of the liner. Hence, in the preferred embodiment the liner material, as initially applied, or after application thereof, also in cludes a small but effective amount of a catalyst to induce the desired polymerization, in situ, after the lining has been applied. Further, and as will also be described in greater detail hereinafter, the liner material, in its preferred embodiments, also contains additional organic polymer or polymerizable compound and finely divided solid material as coloring pigment or to contribute other or additional desirable physical characteristics.

Other objects, features and advantages of the invention will appear more clearly from the following detailed description thereof and, in this regard, and asalluded to above, it should be understood that whereas the invention is described herein principally in connection with the filling of tooth cavities, it additionally finds utility in other dental and medical work and procedures. For example, the composition and process can be used on external tooth surfaces so that Orthodontists can provide improved attachment of appliances. Further, the invention enables periodontists -to use improved splinting techniques and prosthodontists to obtain better results in the cementing of abutments. Still further, the composition can be used by general practitioners to provide increased cavity prevention by using the composition for the filling of developmental pits and fissures in teeth which, if not treated, could eventually result in cavities. Also, because bone tissue is quite similar to tooth tissue, the present invention can find utility by orthopedic surgeons for the repair of diseased, damaged or deformed bone structures. Moreover, the unsaturated organic phosphoryl monofluorides can find utility as intermediate or primer coatings to provide a better bonding of acrylic or the like materials to metal surfaces.

At present, the strong trend in dentistry is to discontinue the use of dental amalgam for the filling of tooth cavities due to its lack of tooth color, which renders it unattractive. In place of dental amalgam it has become the trend to use organic resins, or more accurately, mixtures of organic resins modified with chemically inert powder material, so as to closely match the color of the tooth filling to that of the tooth. The filling resins most commonly used in dentistry at the present time are methylmethacrylate monomer, with lesser or greater amounts of related compatible monomeric or dimeric materials, together with varying amounts of powder fillers, as aforesaid, sometimes treated with silanes, the general characteristics of which are described in U.S. Pat. Nos. 3.066,1l2, 3,194,783 and 3,503,128. As has already been mentioned, however,

the chief difficulty with these resinous filling compositions, just as was and is a difficulty with dental amalgam, is that of attaining a really strong leak-proof bond between the filling and the tooth. The present invention, in its most preferred embodiment and application, contemplates not the total replacement of the currently used resinous filling compositions but rather the supplementation thereof by first lining the tooth cavity with the composition and process of this invention and then using the aforedescribed currently marketed resinous filling compositions, or other resinous compositions, to fill the remainder and generally the bulk of the cavity. In effect, therefore, the liner functions as a transition layer at the interface of the filling with the tooth which layer provides a superior bond and seal with the tooth structure and also a good bond with the remainder of the filling composition which fills the bulk of the cavity. As indicated above, but to elaborate on the point, the liner which functions as this transitional layer can, if desired, be applied with the polymerizable organic phosphoryl monofluoride already in a substantially fully polymerized state this by dissolving the liner composition, i.e, the polymeric constituents thereof, in a suitable solvent to provide the desired viscosity whereby, after application the solvent rapidly evaporates leaving the solid constituents of the linear bonded to the tooth tissue. However, when, as in the. preferred embodiment, the organic phosphoryl monofluoride of the liner is in a nonpolymerized, or not totally polymerized, state as the liner is applied to the tooth, there can, by way of the subsequent polymerization thereof in situ, be copolymerization and crosslinking between the liner and the polymerizable ingredients of the remainder of the tooth filling whereby the resulting transitional layer provides the ultimate in bond strength not only with the tooth tissue but also with the composition forming the bulk'of the filling.

As indicated above, the embodiment of the liner composition of this invention which is most preferred,

on the basis of results to date, contains at least one and preferably a plurality of methacrylic groups as the addition polymerizable sites. Illustrative is glycerol dimethacrylate monoester of monofluorophosphorie acid:

Typical of other organic phosphoryl monofluories incorporating a methacrylate group and serving well for the practice of the invention is ethylene glycolmonomethacrylate monofluorophosphate Y en c c 0 crt c11 0 1? F cn on Howeven riumerous other addition polymerizable or-; I ganic radicals can be used in place of the methacrylici group, examples of which can best be given with refer ence to the method whichcan be used for making. the i v ester. i

Reference is here made to US. Pat. No. 2,712,548, I issued July 5, l955 toArchie Hood, whichpatent dekl scribes a method which can be used for manufacture of organic esters of monofluoropho sp horicacid. Their'eaction is as follows:

ROH+HPO5 F2 R o Po nr HF and preferably one wherein the unsaturation is present in the form of one or more vinyl typegroups. The alco-a hol used can be a simple, unsaturated monohydric ali-, I phatic alcoholof which the following are examples. 5

Allyl Alcohol Metallyl Alcohol (i.e. 2-methyl-2-propen-l-o'l.)

3-Buten-l-ol. V

I-Hexen-3-ol.

4 Methyl-3 Penteri-Q-ol. I The alcohol used can, and on the basis of my work, to

date preferably should, containiacrylate or rnethacrylate groups, of which the following are examples;

1. 2 hydroxy ethyl methacrylate (or acrylate,-i.e. the A i acrylate canibe used instead of the methacrylate) glycol mono methacrylate (or acrylate) 2. glycerol dimethacrylate. 3. dimethacrylate 4. tri-methylol propane-dimethacrylate The alcohol used can contain other chemical groups or I elements, an example being cinnamic alcohol. (i.e. 3-. phenyl -2 propen-l -ol). For preparation of the addition polymerizablephosphoryl monofluoride the compound used for the esterification reaction need not be an alcohol but it must, of course, react as or like an alcohol insofar as esterification reactionsare concerned. An example of such a compound is glycidyl methacrylate. Hence such compounds are intended to becomprehendedby the term alcohol in my description .ofthe,

manner of preparation of the phosphoryl monofluoride esters.

Based on theory and results to date, it is generally preferred that the aliphatic chain not contain more than 8 carbon atoms. Further, and as indicatedabove, preferredare the aliphatic or, aromatic monohydric alcohols containing one or more substituted polymerization groups, ideally methacrylate or acrylate groups."

It should be noted that the above description andin' all the examples given of the R radical of the phos phoryl monofluoride, only carbon, hydrogen and oxya gen atoms are presentdnvestigation to date indicates. that such esters of monofluorophosphoric acidare non-;

toxic, and though I do not wish to infer that other atoms cannot, for the practice of the invention, be present in. the organic radical, .I prefer, on the basis of workto date, that;the 'organicradical of the monofluorophos-- phoric acid contain no atoms other than hydrogen, oxygen and carbon simply on the grounds that the pr'es ence of other atoms could conceivably raise toxicity problems.

As indicated previously, the esters of the monofluorophosphoric acid for the practice of the present invention can be prepared in accordance with the teachings of the aforedescribed United States patent to Archie Hood. For purposes of illustration the follwing is a specific example.

To approximately 100 grams of Z-hydroxyethyl methacrylate was added, dropwise, about 120 grams of freshly distilled difluorophosphoric acid (HPO F and reaction allowed to occur at room temperature, with stirring for approximately 12 hours at about. 25C. A flush of dry nitrogen was maintained during addition and during the 12 hour reaction period. The resulting product was vacuum distilled to remove the excess difluorophosphoric acid. Then the product was freed of any remaining difluorophosphoric acid by the addition of sodium hydroxide to precipitate the sodium salt of the ester, which after separation by filtration, is washed with absolute ethyl alcohol to remove impurities. The free ester can be regenerated from its sodium salt by mineral acid addition followed by extraction with acetone.

As has already been indicated, the preferred tooth cavity lining compositions of this invention comprise a mixture of the polymerizable organic ester of the monofluorophosphoric acid with other ingredients. These additional ingredients include the following: (1) resin binder, i.e. additional polymerized or polymerized organic compound; (2) finely divided filler or pigment material; and (3) catalyst for the polymerizable organic monofluorophosphate and for the additional polymerizable material. Still further, the lining composition should preferably include minor amounts of other ingredients such as stabilizers, levelling agents and brighteners. The following specific liner composition, along with explanation of the function of the various ingredients, will serve to illustrate, all percentages being by weight.

A. Resin binder and related ingredients approximately 18% of the total solids and consisting essentially of:

1. a mixture of 47 percent bis (Z-methacryloxethyl) isophthalate, 38 percent bis (2-methacryloxyethyl) phthalate and percent bis (2- methacryloxyethyl) terephathalate.

2. monomeric methyl methacrylate to reduce viscosity, 10 percent of 1. above.

3. dodecyl mecaptan as a polymerization accelerator, 0.5 percent of 1.

4. methacrylic acid as a stabilizer, 0.3 percent of 5. 2, 6-di-tertiary butyl p-cresol as a stabilizer, 0.2

percent of l.

6. N, N, diemthyl 3, 5 dimethylaniline as a polymerization accelerator, 0.7 percent of l.

7. dimethylpolysiloxane as a levelling agent, 5 ppm based on 1.

8. glycerol diemethacrylate monofluorophosphate,

10 percent based on 1.

9. gamma methacrypropyltrimethoxysilane 0.5

percent based on 1.

B. Finely divided solid material as pigment and filler,

approximity 82 percent of the total solid material and consisting essentially of:

l. Finely divided quartz powder, 5 micron or less particle size.

2. Titanium dioxide, magnesium oxide and calcium oxide, in approximately equal proportions as a brightener, 3 percent of l. (i.e. the quartz powder).

C. Solvent consisting of a mixture, in equal molar amounts of acetone and chloroform, sufficient to provide a pastelike viscosity to the liner composition.

D. Benzoyl Peroxide, as polymerization catalyst, about 1 percent based on 1, 2 and 8 of Part A.

In practice the catalyst, i.e. part C, is mixed with the solid ingredients which constitute part B and the solvent can be mixed with either part A or part B whereby there is a two part mix which, upon mixing, commences to polymerize. These two parts can be encapsulated in a two-compartment encapsulation, of appropriate size to be accommodated in mixers well known in the art of dentisty. Hence, the two parts can be most thoroughly mixed by the dentist just prior to application to the tooth cavity.

It will be understood, of course, that the above constitutes a very specific example of a composition embodying the invention and that various of the ingredients can be excluded and, alternatively, additional ingredients can, if desired, be included. Typical of the latter would be the inclusion of an ultraviolet light absorber, such as 2-hydroXy-4-methoxy benzophenone, to prevent yellowing. In accordance with the invention, the key ingredient is, of course, the ester of the monofluorophosphate, and it should be noted that it need only be present in relatively small percentage of the total resin or polymerizable solids of the composition as one percent of the resin solids being sufficient to provide significantly increased bonding. As further points of particular note in conjunction with the above specific example, the quartz powder functions as a strengthening filler having a coefficient of thermal expansion which is such that the coefficient of thermal expansion of the aggregate of the solid ingredients in the liner material substantially matches the coefficient of thermal expansion of the tooth. The quartz powder can preferably be treated with a silane to provide a surface on the quartz particles to increase the bond strength thereof and the resin. Such treatment of quartz, as a filler, is already known in the dental art. Also already known in the dental art is the use of silanes, such as gamma-methacryloxypropyltrimethoxysilane in dental fillings as keying or coupling agents. Reference has been made above to patents teaching such silanes for use in dental fillings. By keying or coupling agent is meant an ingredient which increases the bond strength of the dental filling and, on this basis, the polymerizable organic phosphoryl monofluoride ingredient in the composition of the present invention could be considered as a substitute, though an improved substitute, for the silanes previously known for this purpose. It bears mention, however, that best results with the present invention have thus far been attained by using the organic phosphoryl monofluoride, in accordance with the present invention, in combination with the silanes heretofore used as coupling or keying agents in that, when the combination is used, there appears to be a synergistic affect. Though, as will be elaborated upon hereinafter, I do have a theory as to the excellent results attainable by way of the use of the polymerizable organic phosphoryl monofluorides, I do not purport to have an explanation for the synergistic effect when such phosphoryl monofluorides are used in combination with the silanes.

Also worthy of mention is the use of the polymerizable organic phosphoryl monofiuorides in combination with other compounds used as keying agents, examples being N-phenyl glycine glycidyl methacrylate and the compounds disclosed in US. Pat. No. 3,200,142 to R. L. Bowen.

It should be understood that various other resins can be used in place of those, and the combination of those, specified in sub-paragraph 1 of paragraph A above in the specific example. Illustrative of the numerous possibilities are ethylene dimethacrylate, tetraethylene glycol, epoxy resin and polyurethane resin. The key point is that the polymerizable organic phosphoryl monofluoride, which constitutes the principal feature of the present invention, can best be used in combination with other polymeric materials rather than as the sole polymeric material which is applied to the tooth tissue, I also wish to reiterate that whereas it is preferred to incorporate the polymerizable phosphoryl monofluoride only in the liner composition which is applied to the tooth tissue, and then fill the remainder of the cavity with conventional resinuous compositions already known in the dental art, it is within the purview of the invention to formulate the entire filling to include the polymerizable organic phosphoryl monofluoride.

To further elaborate on what has been stated above, in the preferred practice of the method of this invention, the liner composition, including the polymerizable organic phosphoryl monofluoride, is first applied to the entire surface of the tooth cavity, after decayed material has been removed and there has been thorough cleansing, and then, after evaporation of theisolvent ingredients, the remainder of the cavity is filled with other resinous composition as described above and is as well known in the art. Where this resinous material used to fill the remainder of the cavity itself contains polymerization catalyst effective to cause polymerization of the polymerizable material of the liner, it is not essential to include catalyst in the liner composition since the catalyst in the bulk of the resinous filling is sufficient to cause the polymerization not just of the bulk of the filling but also of the liner. However, for optimum control, and also flexibility in the choice of the material used for filling the bulk of the cavity, it is preferred that polymerization catalyst for the liner be included in the liner composition itself so that the liner composition is self catalyzing whereby polymerization of the liner is assured independent of any, catalyzed polymerization of the remainder of the cavity filling.

I have indicated above that the quartz ingredient performs a function, in addition to that of adding strength, in tending to match the coefficient of thermal expansion of the liner to that of the tooth. But much .preferred as a filler, in this regard, is lithium aluminum silicate (which can be in one or more of its geologic forms such as beta-eucryptite, beta-spodumene, petalite etc.) which have a negative coefficient of thermal expansion and, hence, the amount of which included in the composition can be adjusted such that, in combination with the amounts and the coefficients of thermal expansion of the other solid ingredients of the lining, the coefficient of thermal expansion of the aggregate lining composition can be caused to very closely match that of the tooth.

It will be understood, of course, that particularly where the polymerization catalyst is included as an in,- I

gredient in the liner compositiomfinal' mixing of the liner composition should only takeiplace just prior to' application of the liner to the tooth. Ideally, and as will be appreciated by those skilled in the art of polymer chemistry, the liner composition should be applied and then, after only sufficient time is given to allow substantially total evaporation of thesolvent in the liner mixture, the remainder of the cavity is filled with the other polymerizable filling composition, whereupon there can be simultaneous polymerization of the liner and the bulk of the filling composition, by way of the attainable controlled timed catalysis, such thatthere results the desired copolymerization and cross linking between the liner, which constitutes the transitional layer, and the y bulk of the filling.

I do not purport to know all of the precise theory which would explain the success of the invention in providing such excellent bond strength with theltooth structure. However, based on my present theory, and

the test results obtained, I believe that the function of I a the key ingredient of the liner can best be described by I I denominating this key ingredient as a surface-active co-i monomer. By this term I me anithat the polymerizable ester of the monofluorophorophosphoric acid is a molecule one end of which is non-polar, and organophillic, I and capable of copolymerization or homopolymeriz I ation, and the other end of which is a polar group which renders the molecule surface active and attracted, for

good bond strength, with the calcium phosphate, hy-

droxyapatite, of the tooth tissue, It is this attraction which may be described as adsorption which results in the adhesion of molecules to a surface; ltis notyet known whether the excellent bonding at the: interface between the tooth andthe liningisr a hybrid ioniccovalent oxane bond between the apatite and the ester or hydrogen bonding between polar groups at the inter- I face surfaces. By either theory, however, therewould likely be an equilibrium making fluoride, ion available as a means of strengthening adjacent tooth structure.

But the key point is that by way of the polar fluorophos- I phate group at one end of the molecule there is excellent adsorption to the tooth tissue resulting in bonding while the polymerizable group at the other end of the molecule results in excellent bonding with ithe remain der of the tooth filling. The end result is a non-toxic tooth filling which, at one and the same time, provides excellent assurance, by way of the good bond strength,

against leakage between the filling-to-tooth tissue interface, which assures against additional tooth caries and which closely matches the tooth tissue in physical properties of both a functional nature and an e'sthetic na- 7 ture.

In all of the above I have sought toindicate that in my' recommendation as to the practice of this invention, by 7 reference to what I consider preferred embodiments, I

have limited myself on the basis of test results to date.

Hence, for example, I have indicated that on the basis' of conceivable toxicity problems, there could be diffir culty in the free substitution of the hydrogen, for example, with other atoms, or combinations of atoms, in the organic radical of the polymerizable phosphoryl mono,-

termine the possible applicability of the di esters of fluorophosphoric acid for the intended purpose as aforesaid. Still further, whereas test results to date indicate that the organic radical of the ester of the fluorophosphoric acid must, for the liner or tooth filling, constitute a polymerizable organic group, and, on the basis of theoretical consideration, I conclude that polymerization of the organic radical, and hence the ability thereof to copolymerize and cross link, constitutes an important feature of the invention, I do not, on the basis of my work to date, desire to necessarily limit the scope of my invention to these features. Still further, whereas to date I have only worked with the free monoesters of monofluorophosphic acid and not with the sodium, potassium, or other salts of such acids, nevertheless the salts can, it is expected, be used if desired and intended to be comprehended by my invention. Hence whereas I have described my invention with reference to preferred embodiments thereof, it should be appreciated that various changes and modifications may be made, and yet within the purview of my invention as defined in the claims which follow.

The embodiments of the invention in which an exclusive property or privilege is claimed are defined as follows:

l. A method for treating teeth or bone tissue including the step of bonding thereto a bone or dental filling composition including at least a small but effective amount of an unsaturated aliphatic addition-polymerizable organic phosphoryl monofluoride thereby to increase the bond strength of said composition to said tis sue, the organic radical of said phosphoryl monofluoride containing only oxygen, hydrogen and carbon atoms.

2. A method as set forth in claim 1 wherein said organic phosphoryl monofluoride contains at least one methacrylic group.

3. A method as set forth in claim 2 wherein said organic phosphoryl monofluoride is glycerol dimethacrylate phosphoryl monofluoride.

4. A method as set forth in claim 1 wherein said composition also includes an organic polymer material other than said addition-polymerizable organic phosphoryl monofluoride.

5. A method as set forth in claim 4 wherein said composition further includes finely divided solid material. 6. A method as set forth in claim 1 wherein said composition also includes catalyst to cause polymerization.

7. A method as set forth in claim 1 wherein said composition also includes another organic polymeric material, finely divided solid material, and a catalyst to cause polymerization.

8. A method as set forth in claim 7 wherein said phosphoryl monofluoride contains at least one methacrylic group and wherein said other organic polymeric material also contains methacrylic groups.

9. A method for filling a tooth cav'ity comprising applying to the walls of the tooth cavity a lining composition comprising an unsaturated aliphatic addition-polymerizable organic phosphoryl monofluoride and then filling the remainder of the cavity with a filling composition including an organic polymeric material, the organic radical of said phosphoryl monofluoride containing only carbon, hydrogen and oxygen atoms.

10. A method as set forth in claim 9 wherein the organic polymeric material in said filling composition and said addition-polymerizable organic phosphoryl monofluoride are caused to simultaneously polymerize in situ after being applied to the tooth.

11. A method as set forth in claim 9 wherein the lining composition also includes a catalyst to cause polymerization.

12. A method as set forth in claim 9 wherein said lining composition also includes finely divided solid material and organic polymeric material other than said addition-polymerizable organic phosphoryl monofluoride.

13. A method as set forth in claim 9 wherein said organic phosphoryl monofluoride contains at least one methacrylic group.

14. A method as set forth in claim 9 wherein said lining composition also contains a silane.

15. a method as set forth in claim 9 wherein the organic phosphoryl monofluoride in said lining composi tion is glycerol dimethacrylic phosphoryl monofluoride.

16. A method as set forth in claim 12 wherein said finely divided material has a coefficient of thermal expansion which causes the coefficient of thermal expansion of the lining composition to substantially match that of the tooth. 

1. A METHOD FOR TREATING TEETH OR BONE TISSUE INCLUDING THE STEP OF BONDING THERETO A BONE OR DENTAL FILLING COMPOSITION INCLUDING AT LEAST A SMALL BUT EFFECTIVE AMOUNT OF AN UNSATURATED ALIPHATIC ADDITION-POLYMERIZABLE ORGANIC PHOSPHORYL MONOFLUORIDE THEREBY TO INCREASE THE BOND STRENGTH OF SAID COMPOSITION TO SAID TISSUE, THE ORGANIC RADICAL OF SAID PHOSPHORYL MONOFLUORIDE CONTAINING ONLY OXYGEN, HYDROGEN AND CARBON ATOMS.
 2. A method as set forth in claim 1 wherein said organic phosphoryl monofluoride contains at least one methacrylic group.
 3. A method as set forth in claim 2 wherein said organic phosphoryl monofluoride is glycerol dimethacrylate phosphoryl monofluoride.
 4. A method as set forth in claim 1 wherein said composition also includes an organic polymer material other than said addition-polymerizable organic phosphoryl monofluoride.
 5. A method as set forth in claim 4 wherein said composition further includes finely divided solid material.
 6. A method as set forth in claim 1 wherein said composition also includes catalyst to cause polymerization.
 7. A method as set forth in claim 1 wherein said composition also includes another organic polymeric material, finely divided solid material, and a catalyst to cause polymerization.
 8. A method as set forth in claim 7 wherein said phosphoryl monofluoride contains at least one methacrylic group and wherein said other organic polymeric material also contains methacrylic groups.
 9. A method for filling a tooth cavity comprising applying to the walls of the tooth cavity a lining composition comprising an unsaturated aliphatic addition-polymerizable organic phosphoryl monofluoride and then filling the remainder of the cavity with a filling composition including an organic polymeric material, the organic radical of said phosphoryl monofluoride containing only carbon, hydrogen and oxygen atoms.
 10. A method as set forth in claim 9 wherein the organic polymeric material in said filling composition and said addition-polymerizable organic phosphoryl monofluoride are caused to simultaneously polymerize in situ after being applied to the tooth.
 11. A method as set forth in claim 9 wherein the lining composition also includes a catalyst to cause polymerization.
 12. A method as set forth in claim 9 wherein said lining composition also includes finely divided solid material and organic polymeric material other than said addition-polymerizable organic phosphoryl monofluoride.
 13. A method as set forth in claim 9 wherein said organic phosphoryl monofluoride contains at least one methacrylic group.
 14. A method as set forth in claim 9 wherein said lining composition also contains a silane.
 15. a method as set forth in claim 9 wherein the organic phosphoryl monofluoride in said lining composition is glycerol dimethacrylic phosphoryl monofluoride.
 16. A method as set forth in claim 12 wherein said finely divided material has a coefficient of thermal expansion which causes the coefficient of thermal expansion of the lining composition to substantially match that of the tooth. 